| CAS No.: | 9003-11-6 |
|---|---|
| Cream Time: | 15-30 Sec |
| Gel Time: | 100-180 Sec |
|
Still deciding? Get samples of US$ 0/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
HFC-Blown Blend Polyols for Rigid Polyurethane Foam PIR Discontinuous Panel
DmcPanel 1814/PIR is a type of blend polyols developed for discontinuous panel. It is developed using HFC-245fa as blowing agent which contains polyether polyol, silicone surfactant, catalysts, flame retardant and other special additives etc. . It has good flowability and flammability compared with PUR foam.
Reaction properties (hand test)
| Item | Unit | Specification |
| DmcPanel 1814/PIR | g | 100 |
| DmcIso 1800 | g | 140-160 |
| Cream time | sec | 15-30 |
| Gel time | sec | 100-180 |
| Free rise density | kg/m3 | 27-29 |
| Item | Unit | Specification | Test standard |
| Core density | kg/m3 | ≥40 | ASTM D1622-08 |
| Thermal conductivity, 20ºC | W/(m.k) | ≤0.024 | ASTM C518-10 |
| Compressive strength | kPa | ≥140 | ASTM D1621-10 |
| Closed cell content | % | ≥90 | ASTM D6226 |
| Water absorb | % | ≤3 | ASTM C209-12 |
| Thermal stability, -30-80ºC | % | ≤1.5 | ASTM D2126-09 |
| Flammability | B2 | DIN 4102 |
The above testing data have been generated in lab or field conditions which are typical for this application. They are believed to be correct but data variations due to varying processing or ambient conditions can not be excluded. The customer remains responsible for making his own interpretation of data and suitability of the chemicals to his particular operation.
220kg/drum for Polyol and 250kg/drum for Isocyanate.